‘Sikalastic P 770’ (formerly known as ‘MasterSeal P 770’) Primer for use with ‘Sikalastic M 808’ (formerly known as ‘MasterSeal M 808 Grey’, and ‘MasterSeal M 808 Light Grey’) topcoats. Site applied coating system, which is light grey coloured (once mixed and applied), comprising of a primer and polyurethane coatings. Coat 1 primer: Mix parts A & B of ‘Sikalastic P 770’ Primer in a weight ratio of 2.2:2.8. Apply as per manufacturer’s IFU ‘version No. 1’, dated ‘22nd November 2024’. Cure for 24 hours@7°C. Coat 2 (coating): Mix parts A & B of ‘Sikalastic M 808’, dark grey coloured (once mixed) polyurethane coating in a weight ratio of 3.3:1.7. Apply as per manufacturer’s IFU ‘version No. 1’, dated ‘22nd November 2024’. Cure for 6 hours@7°C. Coat 3 (water contact coating): Mix parts A & B of ‘Sikalastic M 808’, light grey coloured (once mixed) polyurethane coating in a weight ratio of 3.3:1.7. Apply as per manufacturer’s IFU ‘version No. 1’, dated ‘22nd November 2024’. Cure for 7 days@7°C. When applying the coating system to GRP there is no need to apply a primer. Mix, apply and cure ‘Sikalastic M 808’ dark grey and then mix, apply and cure ‘Sikalastic M 808’ light Grey (water contact layer) as detailed above. For use with water up to 23°C.
‘Sikadur 31 DW Rapid for use with Combiflex TF Tape’. Site applied, grey coloured two-component epoxy resin for use with grey coloured TPE Tape. Mix parts A & B of ‘Sikadur 31 DW Rapid’ in a 3:1 weight ratio and apply as per product data sheet ‘March 2021, Version 01.03’. Immediately apply ‘Combiflex TF Tape’ as per product data sheet ‘May 2021, Version 01.01’ and cure for 7 days@7°C. For use with water up to 23°C. This material is only approved for the mixing and curing conditions that appear on the approval. If the mix and/or cure conditions are varied from those specified on the approval then the material is not covered by the scope of the approval.
‘Sikadur 31 DW for use with Combiflex TF Tape’. Site applied, grey coloured two-component epoxy resin for use with grey coloured TPE Tape. Mix parts A & B of ‘Sikadur 31 DW’ in a 3:1 weight ratio and apply as per product data sheet ‘February 2022, Version 03.03’. Immediately apply ‘Combiflex TF Tape’ as per product data sheet ‘May 2021, Version 01.01’ and cure for 7 days@7°C. For use with water up to 23°C. This material is only approved for the mixing and curing conditions that appear on the approval. If the mix and/or cure conditions are varied from those specified on the approval then the material is not covered by the scope of the approval.
‘Sika Monotop 1010’ primer for use with ‘Sika Monotop 4012’ cement mortar. Site applied, grey coloured cementitious, polymer modified coating material used as bonding primer and cementitious, fibre reinforced, low shrinkage repair mortar. First coat: Mix 25kg ‘Sika Monotop 1010’ with 5.25 litres of water and apply as per manufacturer’s ‘Sika Monotop 4012' IFU issue no. ‘001’ dated ‘July 2022’. Second coat: Mix 25kg ‘Sika Monotop 4012’ with 3.8 litres of water and apply immediately to the first coat as per manufacturer’s IFU issue no. ‘001’ dated ‘July 2022’. Cure for 21 days@7°C. For use with water up to 23°C. This material is only approved for the mixing and curing conditions that appear on the approval. If the mixing and/or curing conditions are varied from those specified on the approval then the material is not covered by the scope of the approval.
‘Sika MonoTop®-1010’, one-part cementitious bonding primer for use with ‘Sika MonoTop®-615’ one-part cementitious repair mortar. Mix ‘Sika MonoTop®-1010’ with tap water in the ratio of 25kg:5.25 litres. Apply as per manufacturer’s Product Data Sheet ‘020302020010000054, March 2021, Version 01.01’. Mix ‘Sika MonoTop®-615’ with tap water in the ratio of 25kg:3.8 litres and apply immediately to ‘Sika MonoTop®-1010’ as per manufacturer’s Product Data Sheet ‘020302040030000198, December 2021, Version 02.02’. Cure for 21 days@7°C. For use with water up to 23°C. This material is only approved for the mixing and curing conditions that appear on the approval. If the mixing and/or curing conditions are varied from those specified on the approval then the material is not covered by the scope of the approval.
Page of 1
We use cookies to give you the best possible experience with WRAS. Some are essential to provide website functions and ensure the website is secure. We also use cookies to help us understand how people use the site and to make improvements. Click "Accept All" to enable recommended settings or click "Manage cookies" to adjust your settings. For more details, see our Cookie Policy.